BESTPOLUX PCG2X/02
| Category: | PC , Polycarbonate |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTPOLUX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gVG99R_BESTPOLUX-PCG2X-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate black lubrified with 10% glass fibre reinforcement and V-0 quality. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.35 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ISO 62 |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3250 | MPa | ISO 527-2 |
| Tensile Stress | 78.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 145 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+15 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viton® B-70 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| AKROMID® B3 GF 15 9 RM-M natural (3679) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| LEXAN™ FXE1414 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Karina GRAY PVC COMPOUND 800-18/121-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OTECH PVC OC5014-Soles | OTECH Corporation | PVC, Unspecified | OTECH PVC |