SABIC® HDPE CC253
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gV084M_SABIC-HDPE-CC253.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE CC253 offers a good combination of stiffness, impact resistance, ESCR and organoleptic properties. The typical applications of this grade are mainly injection moulding and compression moulding of caps for sparkling water and carbonated soft drinks. SABIC® HDPE CC253 does not contain slip agent. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1100 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 26.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 30.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 200 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1150 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 26.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Compression Molded) | 7.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 124 | °C | ISO 306/A |
| Melting Temperature (DSC) | 131 | °C | ISO 11357-3 |
| Enthalpy Change | 201 | J/g | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLOY® PG-0030N | Nytex Composites Co., Ltd. | PP, Unspecified | NYLOY® |
| ALCOM® PWL 10/1.1 AS UV WT1127-11LB | ALBIS PLASTIC GmbH | PC | ALCOM® PWL |
| APEX® 89-P334-A | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina BLACK PVC COMPOUND 853-48/ 1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| NYLOY® AT-0060N | Nytex Composites Co., Ltd. | PS (GPPS) | NYLOY® |