ULTEM™ AR9110 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gUrTPB_ULTEM-AR9110-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 13 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4480 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 106 | MPa | |
| Break | 102 | MPa | |
| Tensile Elongation 3(Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 4830 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 189 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (3.20 mm) | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 208 | °C | ASTM D648 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| FAA Flammability 6 | NATURAL | FAR 25.853 | |
| NBS Smoke Density | ASTM E662 | ||
| Flaming, Dmax | 5.00 | ||
| Flaming, Ds, 1.5 min | 0.00 | ||
| Flaming, Ds, 4 min | 5.00 | ||
| OSU Peak Heat Release Rate 7 | 36.0 | kW/m² | FAR 25.853 |
| OSU Total Heat Release 8 | 6.00 | kW·min/m² | FAR 25.853 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 343 to 366 | °C | |
| Middle Temperature | 354 to 377 | °C | |
| Front Temperature | 366 to 388 | °C | |
| Nozzle Temperature | 360 to 382 | °C | |
| Processing (Melt) Temp | 366 to 388 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Method A/B |
| 7 . | 5 minute test |
| 8 . | 2 minute test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ChronoThane™ P 80A | CardioTech International, Inc. | PUR-MDI | ChronoThane™ |
| GLS PP ZT89 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| IZTAVIL P-455 | Mexichem Corporativo | PVC Homopolymer | IZTAVIL |
| Petlon Prime B1-G50-00-NT | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |
| POLYelast TPE EC90 D50 P05B | Polykemi AB | PP+EPDM | POLYelast |