Stat-Tech™ NN-40CF/000 NH FRV0 Natural
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Stat-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gUqcbT_Stat-Tech-NN-40CF-000-NH-FRV0-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber for low to high levels of conductivity depending upon application requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.050 to 0.20 | % | |
| Across Flow | 2.3 to 2.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 185 | MPa | ASTM D638 |
| Tensile Elongation 1(Break) | 1.3 | % | ASTM D638 |
| Flexural Modulus | 25900 | MPa | ASTM D790 |
| Flexural Strength | 345 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 50 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | > 245 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 10 to 1.0E+4 | ohms·cm | ASTM D257 |
| Charge Decay Time - (Mil-B-81705C), 12% RH, 5000kV to 50kV | 2 | msec | |
| Shielding Effectiveness | |||
| 10GHz, 1/8" thickness | 70 | dB | |
| 1GHz, 1/8" thickness | 32 | dB | |
| 5GHz, 1/8" thickness | 53 | dB |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 5VB | ||
| 3.00 mm | V-0 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 850 | °C | |
| 1.50 mm | 850 | °C | |
| 3.00 mm | 850 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP462R | LyondellBasell Industries | PP Homopolymer | Moplen |
| Chemical Resources RPP 5500CW | Chemical Resources, Inc. | PP Random Copolymer | Chemical Resources |
| Clariant PC PC-1100G10 | Clariant Corporation | PC | Clariant PC |
| LONGLITE® PMC T 376 JX | CCP Group | Phenolic | LONGLITE® PMC |
| ESTOPLAST XU 150BB21 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |