Advanced Composites ATX832N
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Advanced Composites, Inc. |
| Trademark: | Advanced Composites |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gUptqG_Advanced-Composites-ATX832N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Advanced Composites ATX832N is a composite polypropylene product, which contains talc filler. It is available in North America. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage (3.00 mm) | 9.0E-3 - 0.011 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -40°C | 5.0 | kJ/m² | ISO 180 |
| 23°C | 28 | kJ/m² | ISO 180 |
| Instrumented Dart Impact 1(0°C) | 36.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 123 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 64.0 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 204 | °C | |
| Middle Temperature | 218 | °C | |
| Front Temperature | 218 | °C | |
| Nozzle Temperature | 216 | °C | |
| Processing (Melt) Temp | 204 - 232 | °C | |
| Mold Temperature | 32.2 - 48.9 | °C | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Injection Pressure: 10% over max fill pressureHolding Pressure: 50 to 60% of max fill pressureInjection Speed: 1 to 3 inches/secScrew RPM: 1 to 2 secs before mold open |
| Note Message | |
|---|---|
| 1 . | 6.70 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R513 NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Ferro PP LPP20BD39WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Halene L 73204T | Haldia Petrochemicals Ltd. | LLDPE | Halene L |
| LUVOCOM® 50-7078/GY | Lehmann & Voss & Co. | PC | LUVOCOM® |
| LNP™ LUBRICOMP™ KFL23LH compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |