Duron PEI 2300
| Category: | PEI , Polyether Imide |
| Manufacturer: | ProPolymers Inc. |
| Trademark: | Duron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gUpnVg_Duron-PEI-2300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Duron PEI 2300 is a 30% glass filled polyetherimide that offers a superior combination of mechanical, electrical, and thermal properties. PEI is inherently flame resistant with low smoke emission. It provides outstanding processability and good chemical resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18mm | 0.20 - 0.40 | % | ASTM D955 |
| Transverse flow : 3.18mm | 0.20 - 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.16 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 165 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 8500 | MPa | ASTM D790 |
| Flexural Strength | 225 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 212 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 210 | °C | ASTM D648 |
| Vicat Softening Temperature | 228 | °C | ASTM D1525 |
| CLTE - Flow | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256: 10 kJ/m²Unnotched Izod Impact, ASTM D256: 40 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MFE® -4 | Huachang Polymer Co., Ltd. | Vinyl Ester | MFE® |
| CP PRYME® Polyethylene PE100LD-2M | Chase Plastics Services Inc. | LDPE | CP PRYME® Polyethylene |
| Ferro PP TPP20AA11BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Later 4E61 | LATI S.p.A. | PBT | Later |
| Latigloss 66 H2 G/50 F2 | LATI S.p.A. | Nylon 66 | Latigloss |