Propafilm™ RGP140
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gUOyOZ_Propafilm-RGP140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Multi-Purpose Film Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with polyolefinic copolymers. RGP is a is a multi-purpose film suitable for packaging a wide range of products either in single web form, or in a lamination to itself or to other substrates. RGP140 may be used singly as an alternative to a lamination. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 129°C, 1 min | 6.0 | % | |
| Across Flow : 129°C, 1 min | -1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.30 | ||
| vs. Itself - Static, Outside/Outside | 0.30 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 3600 | µm | |
| Secant Modulus 1 | ASTM D882 | ||
| 1% Secant, MD | 2490 | MPa | |
| 1% Secant, TD | 2090 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield | 230 | MPa | |
| TD : Yield | 190 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break | 90 | % | |
| TD : Break | 130 | % | |
| Seal Strength 4 | 0.14 | N/mm | Internal Method |
| Seal Initiation Temperature 5 | 116 to 146 | °C | Internal Method |
| Oxygen Permeability (23°C, 0% RH) | 35 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 4.0 | g/m²/24 hr | ASTM F1770 |
| Corona Treatment | 38 | dyne/cm | Internal Method |
| Yield | 31.4 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 100 | ASTM D2457 | |
| Haze 6 | 2.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 10%/min |
| 2 . | 50%/min |
| 3 . | 50%/min |
| 4 . | 225°F; 1sec; 15lb/in²; untreated to untreated |
| 5 . | 2secs; 15lb/in²; untreated to untreated |
| 6 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M1053 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Next Nylon 66 Prime Series PX-01BL | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Lucky Enpla LGF6300 | Lucky Enpla Co LTD | PP, Unspecified | Lucky Enpla |
| MAGNUM™ 1250 BG | Trinseo | ABS | MAGNUM™ |
| SQUARE® LSR6039-40JT | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |