DP-11-90 is an unfilled, low viscosity, quick setting two component urethane system. An easy to use 1 to 1 mix ratio (Part A/Part B), DP-11-90 offers the user a 3 minute working time with parts demoldable in as little as 30 minutes. When properly cured, DP-11-90 will exhibit high impact strength and yield thermoplastic-like parts. Some outstanding features include the following:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Specific Volume | 0.910 | cm³/g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Heat Distortion | |||
| @ 24 hr room temperature cure | 63 | °C | |
| @ room temperature cure + 1 hr @ 150°F | 79 | °C | |
| @ room temperature cure + 1 hr @ 200°F | 88 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1 | 3.0 | min | ASTM D2471 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.25 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 to 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation (Break) | 11 | % | ASTM D638 |
| Flexural Modulus | 2040 | MPa | ASTM D790 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity | ASTM D2393 | ||
| -- 2 | 300 | cP | |
| -- 3 | 450 | cP | |
| -- 4 | 176 | cP | |
| Demold Time (25°C) | 30 to 60 | min |
| Note Message | |
|---|---|
| 1 . | 200 gms |
| 2 . | Mixed |
| 3 . | Part B |
| 4 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ B70 G25 NC025 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| HiFill® PBT 1225 L BK | Techmer Engineered Solutions | PBT | HiFill® |
| IDI SMC S10 (Glass Content 30%) | IDI Composites International | TS, Unspecified | IDI SMC |
| Petrotene® PP A2 T20 PRTA011 PH202 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Sylvin 6250-82 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |