INLUBE PA66TF13SI2IM

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Infinity LTL Engineered Compounds
Trademark:	INLUBE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	gTqe4K_INLUBE-PA66TF13SI2IM.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Inlube PTFE, silicone, MoS2 and graphite internally lubricated compounds

Offered in all Infinity base resins and can be combined with reinforcements and process additives

Provide reduced coefficient of friction and low wear, including enhanced mechanical and thermal propertie

General Information
Additive	Impact Modifier PTFE Lubricant (13%) Silicone Lubricant (2%)
Features	Good Wear Resistance Impact Modified Low Friction Lubricated

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.16	g/cm³	ASTM D792
Specific Volume	0.863	cm³/g
Molding Shrinkage - Flow	1.6 to 1.8	%	ASTM D955
Water Absorption (24 hr)	1.2	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	37.9	MPa	ASTM D638
Tensile Elongation (Yield)	12 to 16	%	ASTM D638
Flexural Modulus	1720	MPa	ASTM D790
Flexural Strength	68.9	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm)	85	J/m	ASTM D256
Unnotched Izod Impact (3.18 mm)	1300	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	54.4	°C	ASTM D648
CLTE - Flow	8.1E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+16	ohms	ASTM D257

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.59 mm)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature	79.4	°C
Drying Time	4.0	hr
Processing (Melt) Temp	260 to 302	°C
Mold Temperature	93.3	°C
Back Pressure	0.345 to 0.689	MPa
Screw Speed	40 to 70	rpm
Vent Depth	0.013 to 0.025	mm

Resin Grade	Manufacturer	Category	Trademark
T-Blend® 5005N-EE	TSRC Corporation	TPE	T-Blend®
Niretan A F20	Soredi S.p.a.	Nylon 66	Niretan A
Kingfa PP-V16	Kingfa	PP, Unspecified	Kingfa
Lifoflex® UV FLAM 40600	Müller Kunststoffe GmbH	TPE	Lifoflex®
MAJORIS GE460 - 6744	AD majoris	PP, Unspecified	MAJORIS