Task® 15
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Task® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gTUbnG_Task-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TASK® 15 is a premium performance urethane resin that exhibits exceptional impact strength when cast in thin-wall sections. TASK® 15 features a gradual cure profile, making it ideal for rotational casting applications. Pot life is 6 minutes and handling time 60 minutes at room temperature. Vibrant colors are possible by adding small amounts of SO-Strong® tint or IGNITE® fluorescent colors. Plastic fully cures with negligible shrinkage and can be machined, sanded and/or painted. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.892 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 75A:100B by weight |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.42 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 869 | MPa | ASTM D638 |
| Tensile Strength (Break) | 18.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | % | ASTM D638 |
| Flexural Modulus | 1170 | MPa | ASTM D790 |
| Flexural Strength | 38.7 | MPa | ASTM D790 |
| Compressive Modulus | 414 | MPa | ASTM D695 |
| Compressive Strength | 37.6 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 47.2 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 6.0 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 600 | cP | ASTM D2393 |
| Demold Time 1(23°C) | 60 | min |
| Note Message | |
|---|---|
| 1 . | Cure Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 502 Phillips Process | Marco Polo International, Inc. | HDPE | MARPOL® |
| Telcar® TL-2545F | Teknor Apex Company | TPE | Telcar® |
| Dynaflex™ G2712-1000-02 | PolyOne Corporation | TPE | Dynaflex™ |
| Geon™ Vinyl Fittings M1030 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Fittings |
| Comco PA6G WAX | Comco Nylon GmbH | Nylon 6 | Comco |