TECHNYL® A 20 V25 BLACK 25
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gT8qR5_TECHNYL-A-20-V25-BLACK-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant polyamide 66, reinforced with 25% of glass fibre, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 0.75 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 6500 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 160 | 120 | MPa | |
| Break | 160 | 120 | MPa | |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 2.0 | 4.0 | % | |
| Break | 2.0 | 4.0 | % | |
| Flexural Modulus | 7500 | 6000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 50 | 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 8.0 | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 0.10 | 0.010 | ohms | IEC 60093 |
| Volume Resistivity | 10 | 0.10 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | 25 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.050 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 375 | 350 | V | |
| Solution B | 350 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Glow Wire Flammability Index (1.60 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 31 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 to 275 | °C | |
| Middle Temperature | 275 to 280 | °C | |
| Front Temperature | 280 to 285 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8602-75 Clear 893 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Axiall PVC 7555 Natural | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Fainplast PVC GS 7802 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Sylvin 8353-98FUV White 1513 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polyethylene HDPE B 5845 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |