Sumitomo Epoxy E 9405H-1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gSsG1e_Sumitomo-Epoxy-E-9405H-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| E-9504H-1 is glass fiber filled epoxy molding compound designed for encapsulation of delicate electrical components as well as large coils. Excellent thermal shock, moldability, and retention of electrical properties under humid conditions are the outstanding features of this material. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (Compression Molded) | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.11 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 82.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 11700 | MPa | ASTM D790 |
| Flexural Strength (Break) | 123 | MPa | ASTM D790 |
| Compressive Strength | 220 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 31 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 13 | kV/mm | |
| -- 3 | 13 | kV/mm | |
| Dielectric Constant 4(1 MHz) | 3.70 | ASTM D2520 | |
| Dissipation Factor 5(1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 190 | sec | ASTM D495 |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| 4 . | Wet |
| 5 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 SCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Network Polymers SBS 1000 | Network Polymers, Inc. | SBS | Network Polymers SBS |
| CompaDur® 121 GK 30 natural (009) | DimeLika Plast GmbH | PBT | CompaDur® |
| Jiangsu Sinarise JO9531 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Karina BLACK PVC COMPOUND 750-48/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |