HANWHA EVA 1159
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gSgf1I_HANWHA-EVA-1159.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA EVA 1159 is manufactured by Dow autoclave high pressure process and designed for variety of extrusion coating application such as thermal film(Laminex film) and flexible film etc. EVA 1159 is well known for its excellent processability and high quality assurance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 28.0 | wt% | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 13.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 920 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Seal Initiation Temperature | 70.0 | °C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 46.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 71.0 | °C | ASTM D3417 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Allowable Coating Speed 1(230°C) | > 5.0 | m/sec |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Neck-in 2(230°C) | 90.0 | mm | |
| Cylinder Zone 1 Temp. | 160 to 220 | °C | |
| Cylinder Zone 3 Temp. | 160 to 220 | °C | |
| Cylinder Zone 5 Temp. | 160 to 220 | °C | |
| Adapter Temperature | 220 | °C | |
| Die Temperature | 220 | °C |
| Note Message | |
|---|---|
| 1 . | 100 m/min line speed, 80 kg/hr output |
| 2 . | 100 m/min line speed, 80 kg/hr output |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 9110 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| CALP FR200GF | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| ICORENE® 1314 | ICO Polymers EMEA, A Division of A. Schulman | LMDPE | ICORENE® |
| Lucky Enpla LAY3000 | Lucky Enpla Co LTD | PC+PBT | Lucky Enpla |
| Sylvin 8960-70 White 1416 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |