CERTENE™ PHF-8
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gSTTMn_CERTENE-PHF-8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PHF-8 is a certified prime grade Polypropylene specially designed for Film EXTRUSON by Tubular Water Quench - TWQ - process. PHF-8 combines excellent processability and good melt thermal stability, with films exhibiting clarity, good impact strength, modulus, good barrier to fats and oils, and good chemical resistance. PHF-8 applications include film for articles requiring excellent see-through clarity such as textiles, soft goods and pastries, pre-cooked foods sterilizable bags, bags to pack cooked foods, and paper over-wrap products. PHF-8 recommended processing temperature is between 210° to 230°C. PHF-8 complies with FDA regulation 21CFR 177.1520 (a)(1) (b) (c)1.1, and most international regulations concerning Polypropylene use in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.907 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - 1% Secant (Injection Molded) | 1380 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus 1 | ASTM D882 | ||
| 1% Secant, MD : 32 µm | 689 | MPa | |
| 1% Secant, TD : 32 µm | 689 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Break, 32 µm | 55.2 | MPa | |
| TD : Break, 32 µm | 37.9 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break, 32 µm | 500 | % | |
| TD : Break, 32 µm | 550 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(Injection Molded) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed, Injection Molded) | 102 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 6(45°, 31.8 µm) | 85 | ASTM D2457 | |
| Haze 7(31.8 µm) | 2.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 2 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 3 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 4 . | Testing performed on ASTM D 638 Type I specimen, molded in accordance with ASTM D 4101. |
| 5 . | Testing performed on ASTM D 638 Type I specimen, molded in accordance with ASTM D 4101. |
| 6 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 7 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKASTER™ F101M | Mando Advanced Materials Co., Ltd. | PBT | TEKASTER™ |
| Tritan™ MP100 | Eastman Chemical Company | Copolyester | Tritan™ |
| NEFTEKHIM PP 1365S (H22S) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| ETILINAS HD6070UA | POLYETHYLENE MALAYSIA SDN BHD | HDPE | ETILINAS |
| MAJORIS EB730 | AD majoris | PP, Unspecified | MAJORIS |