LNP™ THERMOCOMP™ MF002S compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gRwpgU_LNP-THERMOCOMP-MF002S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP MF002S is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound MFX-1002 HS Product reorder name: MF002S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 0.960 | g/cm³ | |
| -- | 0.968 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 7.0E-3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.015 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2980 | MPa | ASTM D638 |
| -- | 2980 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 46.0 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2/5 |
| Break | 51.7 | MPa | ASTM D638 |
| Break 3 | 42.0 | MPa | ASTM D638 |
| Break | 44.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.7 | % | ASTM D638 |
| Yield | 4.4 | % | ISO 527-2/5 |
| Break | 3.7 | % | ASTM D638 |
| Break 5 | 6.7 | % | ASTM D638 |
| Break | 5.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- | 2870 | MPa | ASTM D790 |
| 50.0 mm Span 6 | 2390 | MPa | ASTM D790 |
| -- 7 | 2340 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.8 | MPa | ASTM D790 |
| -- | 64.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 39 | J/m | ASTM D256 |
| 23°C 8 | 5.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D4812 |
| 23°C 9 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 4.80 | J | ASTM D3763 |
| -- | 1.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 154 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 146 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 113 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 99.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.8E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFILL H 15 20 T0 | RIALTI Srl | PP Homopolymer | RIALFILL |
| Polymer-E F8101 | Asia Polymer Corporation (APC) | LDPE | Polymer-E |
| Badaprene® TPV 55A 1049 | Bada AG | PP+EPDM | Badaprene® |
| Jampilen HP500L | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Loyblend® TA-1200 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |