Badadur® PBT8
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Bada AG |
| Trademark: | Badadur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gRuK19_Badadur-PBT8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity, standard injection moulding grade with good mechanical properties |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 2650 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Yield, 23°C) | 57.0 | MPa | ISO 527-2/50 |
| Tensile Strain 3(Yield, 23°C) | 4.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 4(23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Stress 5(23°C) | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength 7 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 8 | ISO 180/1A | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 9 | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 10 | 223 | °C | ISO 3146 |
| CLTE 11 | DIN 53752 | ||
| Flow : 4.00 mm | 1.4E-4 | cm/cm/°C | |
| Transverse : 4.00 mm | 1.4E-4 | cm/cm/°C | |
| Maximum Service Temperature | |||
| 20000 hrs | 120 | °C | |
| some hours | 160 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 12 | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity 13 | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength 14 | 24 | kV/mm | IEC 60243-1 |
| Relative Permittivity 15(1 MHz) | 3.20 | IEC 60250 | |
| Dissipation Factor 16(1 MHz) | 0.018 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm 17 | HB | ||
| 1.60 mm 18 | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | Test Specimen accordng to ISO 3167, Type A |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 80 x 10 x 4 mm |
| 8 . | 80x10x4 mm |
| 9 . | 110x10x4mm |
| 10 . | 10 K/min, compound for moulding |
| 11 . | >=10x10x4 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 80x80x1 mm |
| 15 . | 80x80x1 mm |
| 16 . | 80x80x1 mm |
| 17 . | 125x13x.8 mm |
| 18 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiprene® 1050 | Resirene, S.A. de C.V. | TPE | Resiprene® |
| Monprene® IN-12985 | Teknor Apex Company | TPE | Monprene® |
| TEREZ PA 6 7750 T | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Hanwha Total TPE SE87 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | TPE | Hanwha Total TPE |
| Edgetek™ PC-20GF/000 Phi Gray 6 | PolyOne Corporation | PC | Edgetek™ |