Ultramid® 8202 HS BK-102
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gRUCub_Ultramid-8202-HS-BK-102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8202 HS BK-102 is an unreinforced, heat stabilized, pigmented black, low viscosity, general purpose injection molding PA6 exhibiting excellent fluidity for filling thin sections. It possesses the combination of strength, stiffness and toughness properties as well as excellent chemical, thermal and abrasion resistance. The heat stabilizer system extends its retention of properties at elevated temperatures. Applications Ultramid 8202 HS BK-102 is generally recommended for applications such as drapery hardware, gears, fittings, furniture casters, bearings, handles, clips and fasteners. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.13 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 1.2 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.6 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.6 | -- | % | ISO 62 |
| Saturation | 9.5 | -- | % | ASTM D570 |
| Saturation, 23°C | 9.5 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.7 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.7 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3100 | 970 | MPa | ISO 527-2 |
| Tensile Strength (Yield, 23°C) | 85.0 | 36.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | ||||
| Yield, 23°C | 4.0 | 16 | % | ASTM D638, ISO 527-2 |
| Break, 23°C | 50 | > 100 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 25 | > 50 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 2830 | -- | MPa | ASTM D790 |
| 23°C | 2650 | 770 | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 108 | 35.0 | MPa | ASTM D790 |
| 23°C | 90.0 | 25.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179 | |
| Notched Izod Impact | ||||
| 23°C | 55 | -- | J/m | ASTM D256 |
| -40°C | 4.0 | -- | kJ/m² | ISO 180 |
| 23°C | 5.5 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 178 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 8.3E-5 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| 6.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.710 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| 6.00 mm | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 285 | °C | |
| Mold Temperature | 65.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1005 MS 2 | RTP Company | PBT | RTP |
| Titalon® 2102GBM | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| Tislamid® PA6 PA6 15 MNF FR | Tisan | Nylon 6 | Tislamid® PA6 |
| Wellamid® MRGF25/15 42H-N1/WE1705-N1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Generic Nylon Copolymer | Generic | Nylon Copolymer | Generic |