| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gR4odC_LNP-COLORCOMP-I1000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP I1000 is an unfilled Nylon 6/12 Also known as: LNP* COLORCOMP* Compound I-1000 Product reorder name: I1000 |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 62.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 4.5 | % | ISO 527-2/5 |
| Break 1 | 100 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 2 | 135 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 55.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 3 | 62.0 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.60 | ||
| 1 MHz | 3.20 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 0.020 | ||
| 1 kHz | 0.020 | ||
| 100 kHz | 0.014 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 27 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | 80*10*4 mm |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven B-328 | Propilven, S.A. | PP Random Copolymer | Propilven |
| RheTech Thermoplastic Polyolefin FT2700-01 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Modified Plastics MN 6/6-FG 30 | Modified Plastics, Inc. | Nylon 66 | Modified Plastics |
| Unichem 1417-013 | Colorite Polymers | PVC, Flexible | Unichem |
| Hyundai EP Adhesives LE130A/1002 | HYUNDAI EP Co., Ltd. | PE, Unspecified | Hyundai EP Adhesives |