SCANAMID 6 B32^E F15
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Polykemi AB |
| Trademark: | SCANAMID 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gPGRIw_SCANAMID-6-B32-E-F15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre-reinforced, Modified |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.20 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | 120 | 70.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 4500 | 3000 | MPa | ISO 178 |
| Flexural Stress | 170 | 95.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -20°C | 10 | -- | kJ/m² | |
| 23°C | 16 | 20 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PE HD0494 | Qenos Pty Ltd | HDPE | Qenos PE |
| Titalon® 2250AF | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| TUFNYL® SXXIC GRANITE GREY | SRF Ltd. | Nylon 6 | TUFNYL® |
| Badamid® A70 L | Bada AG | Nylon 66 | Badamid® |
| Chemlon® 257 H | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |