Celstran® PPS-GF50-01 AD3002 Black
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gOxpmG_Celstran-PPS-GF50-01-AD3002-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% long strand glass fiber reinforced polyphenylene sulfide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.72 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.10 - 0.20 | % | ASTM D955 |
| Transverse flow | 0.30 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 21400 | MPa | ASTM D638 |
| 23°C | 20200 | MPa | ASTM D638 |
| -- | 19000 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, -40°C | 180 | MPa | ASTM D638 |
| Fracture, 23°C | 177 | MPa | ASTM D638 |
| Fracture | 165 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, -40°C | 0.95 | % | ASTM D638 |
| Fracture, 23°C | 1.0 | % | ASTM D638 |
| Fracture | 1.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 18500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 280 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 28 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 282 | °C | ASTM D648, ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 70.0 - 80.0 | °C | |
| Rear Temperature | 285 - 295 | °C | |
| Middle Temperature | 290 - 300 | °C | |
| Front Temperature | 295 - 305 | °C | |
| Nozzle Temperature | 290 - 300 | °C | |
| Processing (Melt) Temp | 300 - 310 | °C | |
| Mold Temperature | 140 - 160 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 300 to 310°CFeed Temperature: 20 to 50°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vibrathane® 8050T | Chemtura | PUR-Ester/TDI | Vibrathane® |
| Titalon® 4715AF | Titan Plastics Compounds Co., Ltd. | Nylon 46 | Titalon® |
| NITRIFLEX N-689 B | NITRIFLEX | NBR | NITRIFLEX |
| DJSilicone NE-131 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Globalene® HP561R | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |