Iupilon® EGN2040DF
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gOvKM3_Iupilon-EGN2040DF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon® EGN2040DF is a Polycarbonate (PC) material filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® EGN2040DF are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.10 to 0.30 | % | |
| Flow : 3.20 mm | 0.10 to 0.30 | % | |
| Water Absorption (Saturation, 23°C) | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 30 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 142 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 138 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiten® CFBM | ITEN INDUSTRIES | Phenolic | Resiten® |
| SCANAMID 66 A12^F | Polykemi AB | Nylon 66 | SCANAMID 66 |
| ISPLEN® PP 064 S1F | REPSOL | PP Homopolymer | ISPLEN® |
| Karina BLACK PVC COMPOUND 700-48/1-B-IS-BZ (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupoy庐 GN5009F | LG Chem Ltd. | PC+ABS | Lupoy® |