LONGLITE® PMC T 373 J60
| Category: | Phenolic , Phenolic |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gOKob7_LONGLITE-PMC-T-373-J60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PMC T 373 J60 is a granular wood flour reinforced phenolic product for injection moulding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | 0.90 - 1.3 | % | ISO 2577 |
| Water Absorption | |||
| 24 hr | 0.30 | % | ASTM D570 |
| 23°C, 24 hr | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 55.0 | MPa | ISO 527-2 |
| -- | 55.0 | MPa | ASTM D638 |
| Flexural Strength | 74.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 170 | °C | ASTM D648, ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength (2.00 mm) | 12 | kV/mm | ASTM D149, IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (2.00 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Spiral Flow, CCP: 51 to 70 cmDensity, ASTM D792 & ISO 1183: 1.41 to 1.43 g/cm³Maximum application temperature, IEC 60216-P1, 50 hr: 200°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 40.0 - 90.0 | °C | |
| Middle Temperature | 40.0 - 90.0 | °C | |
| Front Temperature | 40.0 - 90.0 | °C | |
| Nozzle Temperature | 85.0 - 105 | °C | |
| Processing (Melt) Temp | 110 - 120 | °C | |
| Mold Temperature | 165 - 195 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | < 1.00 | MPa | |
| Screw Speed | 30 - 50 | rpm |
| Injection instructions |
|---|
| Injection Time: 5 ± 2 secHardening Time: 15 ± 5 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ABS Proquigel EP-3510 | Proquigel | ABS | ABS Proquigel |
| Formolene® L62009X | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| GAPEX® RPP30EA36HB | Ferro Corporation | PP Homopolymer | GAPEX® |
| HiFill庐 PA6 GF20 RM BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Kumho SSBR SOL-6270SL | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |