MEGOLON™ S340

Category:	TP, Unspecified , Thermoplastic
Manufacturer:	AlphaGary
Trademark:	MEGOLON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	gO7rUd_MEGOLON-S340.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

MEGOLON™ S340 is a thermoplastic, halogen free, fire retardant cable sheathing compound for general purpose applications. MEGOLON™ S340 exhibits an enhanced fire test performance with a high oxygen index whilst retaining similar mechanical properties to MEGOLON™ S300

APPLICATIONS

UK: BS 7655:6.1 types LTS1 and LTS3, BS7878:7 (HD 624.7 S1) and LUL SE569. MEGOLON™ S340 also meets the requirements of BS 7655:4.1 type TM1 for a general purpose PVC sheathing compound

Germany: DIN VDE 0207, part 24, type HM2

France: Norme Francaise NF C 32-323

General Information
Features	Flame Retardant General Purpose Halogen Free
Uses	Cable Jacketing General Purpose
Agency Ratings	BS 7655 4.1 type TM1 BS 7655:6.1 Type LTS 1 BS 7655:6.1 Type LTS 3 BS 7878:7 (HD 624.7 S1) DIN VDE 0207, Part 24, Type HM2 NFC 32-323
Forms	Pellets
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.55	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (150°C/21.6 kg)	4.5	g/10 min	ISO 1133
Mooney Viscosity (ML 1+4, 140°C)	45	MU	ASTM D1646

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	58		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress
-- ¹	18.0	MPa	IEC 60811-1-2
--	14.5	MPa	IEC 60811-1-1
Tensile Strain
Break ²	120	%	IEC 60811-1-2
Break	150	%	IEC 60811-1-1
Elongation at Break
after 4 hours, in IRM 902 Oil : 70°C	170	%
after 7 days, in IRM 902 Oil : 23°C	140	%
after 7 days, in IRM 903 Oil : 23°C	150	%
Tensile Strength
after 4 hours, in IRM 902 Oil : 70°C	13.0	MPa
after 7 days, in IRM 902 Oil : 23°C	13.0	MPa
after 7 days, in IRM 903 Oil : 23°C	11.5	MPa

Thermal	Nominal Value	Unit	Test Method
Cold Elongation (-25°C)	65	%	IEC 60811-1-4
Cold Impact (-25°C)	pass		IEC 60811-1-4
Hot Deformation (90°C)	2.0	%	BS 6469 99.1
Hot Pressure Test (80°C)	15	%	IEC 60811-3-1

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance			BS 6469 99.2
20°C	1.0E+14	ohms·cm
after 12 hours immersion in water : 20°C	5.0E+13	ohms·cm

Flammability	Nominal Value	Unit	Test Method
Acid Gas Emission Conductivity	28.0	µS/cm	IEC 60754-2
Acid Gas Emission pH	4.30		IEC 60754-2
Flammability Temperature Index	300	°C	ISO 4589-3
Smoke Density			ASTM E662
Flaming mode ³	< 120	Ds
Non-flaming mode ⁴	< 270	Ds
Toxicity	2.00		NES 713

Additional Information	Nominal Value	Unit	Test Method
Halogen Acid Gas Evolution	0.0	%	IEC 60754-1
Ozone Resistance	pass		ASTM D470

Extrusion	Nominal Value	Unit
Draw Down	1.5:1.0
Extruder Screw Compression Ratio	1.0:1.0 to 2.0:1.0

Elastomers	Nominal Value	Unit	Test Method
Tear Strength	5.00	kN/m	BS 6469 99.1

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air (100°C, 168 hr)	26	%
Change in Tensile Strain at Break in Air (100°C, 168 hr)	-23	%
Change in Tensile Stress
23°C, 168 hr, in IRM 902 Oil	-10	%
23°C, 168 hr, in IRM 903 Oil	-20	%
70°C, 4 hr, in IRM 902 Oil	-10	%
70°C, 168 hr, in Water	0.0	%	BS 6469 99.1
Change in Tensile Strain at Break
23°C, 168 hr, in IRM 902 Oil	-10	%
23°C, 168 hr, in IRM 903 Oil	0.0	%
70°C, 4 hr, in IRM 902 Oil	10	%
70°C, 168 hr, in Water	-15	%	BS 6469 99.1
Change in Volume
23°C, 168 hr, in IRM 902 Oil	1.0	%
23°C, 168 hr, in IRM 903 Oil	10	%
70°C, 4 hr, in IRM 902 Oil	3.0	%

Electrical	Nominal Value	Unit	Test Method
Dielectric Constant (50 Hz)	4.80		ASTM D150
Dissipation Factor (50 Hz)	0.020		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	40	%	ISO 4589-2

Extrusion	Nominal Value	Unit
Drying Temperature	60.0 to 70.0	°C
Cylinder Zone 1 Temp.	135	°C
Cylinder Zone 2 Temp.	140	°C
Cylinder Zone 3 Temp.	145	°C
Cylinder Zone 4 Temp.	150	°C
Cylinder Zone 5 Temp.	160	°C
Melt Temperature	165 to 175	°C
Die Temperature	165	°C

Note Message
1 .	after 7 days at 100°C
2 .	after 7 days at 100°C
3 .	Time to maximum: 10 minutes
4 .	Time to maximum: 13 minutes

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC T122	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
RTP 803 CC	RTP Company	Acetal (POM) Copolymer	RTP
Sindustris PBT SG3181S	Sincerity Australia Pty Ltd.	PBT+PET	Sindustris PBT
Daelim Po1y® LD-63	DAELIM INDUSTRIAL CO., LTD.	LDPE	Daelim Po1y®
Lutene® XL2902BK	LG Chem Ltd.	PE, Unspecified	Lutene®