Monprene® CP-33142 XRD1 (PRELIMINARY DATA)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gNA9hx_Monprene-CP-33142-XRD1-PRELIMINARY-DATA-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Monprene CP-33142 CLR is a clear, UV resistant thermoplastic elastomer designed for a variety of consumer product applications requiring a soft, rubber-like feel. Monprene CP-33142 CLR is a low hardness, low density grade that exhibits medium flow characteristics, suitable for injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.888 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 44 | ASTM D2240 | |
| Shaw A, 5 seconds | 42 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 1.34 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 1.52 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 2.21 | MPa | ASTM D412 |
| Flow : 300% strain 4 | 2.50 | MPa | ASTM D412 |
| Tensile Strength 5 | ASTM D412 | ||
| Transverse flow : Fracture | 7.30 | MPa | ASTM D412 |
| Flow : Fracture | 6.94 | MPa | ASTM D412 |
| Tensile Elongation 6 | ASTM D412 | ||
| Transverse flow : Fracture | 710 | % | ASTM D412 |
| Flow : Fracture | 680 | % | ASTM D412 |
| Tear Strength 7 | ASTM D624 | ||
| Transverse flow | 25.4 | kN/m | ASTM D624 |
| Flow | 24.2 | kN/m | ASTM D624 |
| Compression Set 8(23°C, 22 hr) | 17 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 182 - 232 | °C | |
| Middle Temperature | 188 - 238 | °C | |
| Front Temperature | 193 - 243 | °C | |
| Nozzle Temperature | 199 - 249 | °C | |
| Processing (Melt) Temp | 199 - 249 | °C | |
| Mold Temperature | 35.0 - 48.9 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 182 - 232 | °C | |
| Cylinder Zone 2 Temp. | 188 - 238 | °C | |
| Cylinder Zone 3 Temp. | 193 - 243 | °C | |
| Cylinder Zone 5 Temp. | 199 - 249 | °C | |
| Die Temperature | 199 - 249 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | C mold, 510mm/min |
| 6 . | Mouth die C, 510mm/min |
| 7 . | C mold, 510mm/min |
| 8 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 GF 15 1 black (2482) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Hostaform® C 9021 S OEK | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LNP™ THERMOCOMP™ RF006EUC compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| SCHULAKETON GF10 | A. Schulman Europe | PK-Aliphatic | SCHULAKETON |
| Moplen RP348S | LyondellBasell Industries | PP Random Copolymer | Moplen |