Epocast 8623-A/Hardener 946
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Huntsman Advanced Materials |
| Trademark: | Epocast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gMvHWo_Epocast-8623-A-Hardener-946.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DESCRIPTION: Epocast® 8623-A/Hardener 946 epoxy syntactic is a two-part, core-filling compound with a soft paste viscosity that provides for easy extrudability through a 1/8-in. (3mm) nozzle. Epocast® 8623-A/Hardener 946 epoxy syntactic is self-extinguishing and cures fast at room temperature, permitting filled edges to be sanded within 3-4 hours. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 0.650 | g/cm³ | ASTM D792 |
| -- 2 | 0.700 | g/cm³ | ASTM D792 |
| -- 3 | 1.00 | g/cm³ | ASTM D792 |
| Solids Content 4 | 100 | % | ASTM D1644 |
| Viscosity | ASTM D2393 | ||
| -- 5 | Paste | ASTM D2393 | |
| -- 6 | Soft-paste | ASTM D2393 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flash Point - COC | ASTM D92 | ||
| -- 7 | 99 | °C | ASTM D92 |
| -- 8 | > 186 | °C | ASTM D92 |
| flammability- self extinguishing time | 30.0 | sec | BMS 5-28 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 1.0 | day | |
| Tensile Lap Shear - etched al/al (25°C) | 11.0 | MPa | ASTM D1002 |
| Weight Gain 9 | ASTM D570 | ||
| Distilled water | 1.5 | % | ASTM D570 |
| Mil-M-5606, hydraulic fluid | 0.40 | % | ASTM D570 |
| Mil-S-3136, Type III test fluid : 25°C | 0.30 | % | ASTM D570 |
| Skydrol 500-A | 0.60 | % | ASTM D570 |
| Work Life - 100 gms (25°C) | 12.0 - 20.0 | min | ASTM D1338 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Modulus | 1030 | MPa | ASTM D695 |
| Compressive Strength (25°C) | 27.6 | MPa | ASTM D695 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Resin | Mixing ratio by weight: 100 | ||
| Hardening method | Mixing ratio by weight: 14 | ||
| Thermoset Mix Viscosity 10(25°C) | 350 | cP | ASTM D2393 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CURE SCHEDULE : 24 hours at 77°F (25°C) or gel at 77°F (25°C), plus 1 hour at 150°F (66°C). |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | System |
| 3 . | Hardener |
| 4 . | System |
| 5 . | Resin |
| 6 . | System |
| 7 . | Hardener |
| 8 . | Resin |
| 9 . | on immersion - 24 hrs |
| 10 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PA66 A1304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Axiall PVC 19920 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Daicel PP PT2N1 | Daicel Polymer Ltd. | PP, Unspecified | Daicel PP |
| Electrafil® PC/ABS 03009 | Techmer Engineered Solutions | PC+ABS | Electrafil® |
| Karina GREEN COLOR CONCENTRATE 40/257-FC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |