Plaslube® POM CO TX10
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gLq1cy_Plaslube-POM-CO-TX10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube®POM CO TX10 is a polyoxymethylene (POM) copolymer product,. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.8 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.17 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 92 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 61.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 9.0 | % | ASTM D638 |
| Flexural Modulus | 2720 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.21 | ASTM D1894 | |
| With steel-static | 0.18 | ASTM D1894 | |
| Wear Factor | 91 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 | °C | ASTM D648 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 188 - 199 | °C | |
| Front Temperature | 182 - 193 | °C | |
| Nozzle Temperature | 177 - 188 | °C | |
| Processing (Melt) Temp | 188 - 204 | °C | |
| Mold Temperature | 76.7 - 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well ventedMoisture Content, as received: Product is packaged at 0.2% or less.Drying not normally required. Dry at 180°F for 1 to 2 hours if necessary. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A HSXW 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| THERMOLAST® K TF9WKF (Series: DW) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Ferro PP NPP00GD01HB BLACK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Flontech® FT-901-D | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| KMI PP KM-003IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |