Tenite™ Propionate 371A4000012 Clear, Trsp
| Category: | CAP , Cellulose Acetate Propionate |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tenite™ Propionate |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gLFRMt_Tenite-Propionate-371A4000012-Clear-Trsp.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Propionate 371-12 contains a mold release and has a plasticizer level of 12%. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.5 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 78 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 31.7 | MPa | |
| Break, 23°C | 33.1 | MPa | |
| Tensile Elongation (Break, 23°C) | 45 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1450 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 41.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 110 | J/m | |
| 23°C | 420 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 83.0 | °C | |
| 1.8 MPa, Annealed | 75.0 | °C | |
| Vicat Softening Temperature 2 | 96.0 | °C | ASTM D1525 |
| CLTE - Flow (23°C) | 1.1E-4 to 1.7E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat (23°C) | 1260 to 1670 | J/kg/°C | DSC |
| Thermal Conductivity (23°C) | 0.17 to 0.33 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+13 to 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 12 to 19 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 3.30 to 3.80 | ASTM D150 | |
| Dissipation Factor (23°C, 1 MHz) | 0.010 to 0.15 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.460 to 1.490 | ASTM D542 | |
| Transmittance (1520 µm) | > 90.0 | % | ASTM E308 |
| Haze (1520 µm) | < 8.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Soluble Matter Loss (23°C) | 0.10 | % | ASTM D570 |
| Weight Loss on Heating - 72 hr (80°C) | 0.40 | % | ASTM D1562 |
| Note Message | |
|---|---|
| 1 . | Conditioned 4 hours at 70°C (158°F) |
| 2 . | Conditioned 4 hours at 70°C (158°F) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Karina WHITE PVC COMPOUND 837-10/ 37-A-ERYB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 65-8347/RD | Lehmann & Voss & Co. | PP Copolymer | LUVOCOM® |
| Sylvin 802-90 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LUVOCOM® 1105-7241-1 | LEHVOSS Group | PEEK | LUVOCOM® |
| Sylvin 8925-80 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |