ExxonMobil™ PP7033N
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | ExxonMobil™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gL4rfG_ExxonMobil-PP7033N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A copolymer resin with high crystallinity, high rigidity and high impact resistance is used in injection molding applications requiring medium melt flow rate, good processability and improved cycle time. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1330 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 25.9 | MPa | ASTM D638 |
| Yield | 25.8 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 5.2 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 1% secant 3 | 1360 | MPa | ASTM D790A |
| 1% secant 4 | 1540 | MPa | ASTM D790B |
| -- 5 | 1260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.7 | kJ/m² | ISO 179/1eA |
| -20°C | 5.3 | kJ/m² | ISO 179/1eA |
| 0°C | 7.3 | kJ/m² | ISO 179/1eA |
| 23°C | 13 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D256A |
| -40°C | 3.9 | kJ/m² | ISO 180/1A |
| -18°C | 4.9 | kJ/m² | ISO 180/1A |
| 23°C | 13 | kJ/m² | ISO 180/1A |
| Dart Drop Impact 6(-29°C, 3.18 mm) | 22.8 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 100 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 91.5 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 52.0 | °C | ISO 75-2/A |
| Legal statement |
|---|
| 未经埃克森美孚化工书面允许，这种产品包括其产品名称，不得在任何医疗应用领域予以使用或有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 13 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Geometry GC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 14CT20-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Grivory® GVX-5 H black 9915 | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Lifoflex® UV FLAM 70600 | Müller Kunststoffe GmbH | TPE | Lifoflex® |
| PLANAC BT-1030-02 | TOYOBO America, Inc. | PBT | PLANAC |
| LEXAN™ HFD1413 resin | SABIC Innovative Plastics | PC | LEXAN™ |