RAMSTER PF350M3
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMSTER |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gKz6B1_RAMSTER-PF350M3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% MINERAL FILLED P.B.T. FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.8 | % | ASTM D955 |
| -- | 1.8 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.50 | % | ASTM D570 |
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 55.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 3.5 | % | ASTM D638 |
| Fracture | 15 | % | ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 95.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 50 | J/m | ASTM D256 |
| 23°C | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 225 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 3.60 | IEC 60250 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 235 - 255 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 245 - 270 | °C | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 30.0 - 105 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefanyl® VR VRGR 925 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 2001Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| ENFLEX VU-424-80A | Ravago Group | PP+EPDM | ENFLEX |
| Grupo IDESA HIPS HI-360-S-01 | Grupo IDESA, S.A. de C.V. | SBC | Grupo IDESA HIPS |
| Lytex 4023 | Quantum Composites Inc. | Epoxy | Lytex |