LNP™ THERMOTUF™ RF006I compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gKBhF4_LNP-THERMOTUF-RF006I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF RF006I is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound RF-1006 HI Product reorder name: RF006I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 1.1 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.27 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.64 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10400 | MPa | ASTM D638 |
| -- | 10800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 161 | MPa | ASTM D638 |
| Break | 179 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.2 | % | ASTM D638 |
| Break | 2.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 8690 | MPa | ASTM D790 |
| -- | 9480 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 248 | MPa | ASTM D790 |
| -- | 267 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 3 | 76 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 17.9 | J | ASTM D3763 |
| -- | 5.66 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 259 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 121 | °C | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® EL-3762 | Sumitomo Bakelite Co., Ltd. | Epoxy | SUMILITE® |
| Generic ABS - Stainless Steel Fiber | Generic | ABS | Generic |
| KumhoSunny PA/ABS HNB0225G4 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+Nylon | KumhoSunny PA/ABS |
| POCAN® BF 4215 000000 | LANXESS Corporation | PBT | POCAN® |
| INEOS EMAA M24N430B | INEOS Olefins & Polymers Europe | EMAA | INEOS EMAA |