SUPRAN® LFT PA A1340
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SAMBARK |
| Trademark: | SUPRAN® LFT PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gIlTAG_SUPRAN-LFT-PA-A1340.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% long glass fiber reinforced polyamide 66. High Stiffness, superior mechanical balanced & heat stable. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D648 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 206 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.9 | % | ASTM D638 |
| Flexural Modulus | 11100 | MPa | ASTM D790 |
| Flexural Strength | 255 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 230 | J/m | |
| 23°C | 220 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 255 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 70.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G1733H-01A | RheTech, Inc. | Nylon 6 | Rhelon |
| Xuchuan XCW-H8926 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Adell Polyamide AO-36 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Chemlon® 113 GX | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Hostaform® XGC25-LW01 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |