Petrothene® GA503028
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gIZ5oh_Petrothene-GA503028.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GA503 is a medium density butene copolymer LLDPE resin with high draw. GA503 is typically selected by customers for stiff, thin blown films. GA503 contains an additive package to minimize discoloration and die build-up. Processing Techniques: GA503 provides high output at low melt temperatures and without high pressure, high torque or shear-induced melt fracture. For improved drawdown without bubble breaks, GA503 can be blended with LDPE. It can also be blended with high performance LLDPE grades to reduce torque and horsepower requirements. Specific recommendations for type of resin and extrusion conditions can be made only when the end use, required properties and processing equipment are known. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 13 µm | 252 | MPa | ASTM D882 |
| 1% secant, MD : 38 µm | 307 | MPa | ASTM D882 |
| 1% secant, TD : 13 µm | 255 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm | 314 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 13 µm | 9.65 | MPa | ASTM D882 |
| MD : Fracture, 38 µm | 33.1 | MPa | ASTM D882 |
| TD : Broken, 13 µm | 7.24 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 23.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 13 µm | 500 | % | ASTM D882 |
| MD : Fracture, 38 µm | 690 | % | ASTM D882 |
| TD : Broken, 13 µm | 630 | % | ASTM D882 |
| TD : Fracture, 38 µm | 740 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709 | ||
| 13 µm, blown film | 30 | g | ASTM D1709 |
| 38 µm, blown film | 110 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 13 µm | 40 | g | ASTM D1922 |
| MD : 38 µm | 100 | g | ASTM D1922 |
| TD : 13 µm | 180 | g | ASTM D1922 |
| TD : 38 µm | 220 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45 °, 12.7 µm, blown film | 60 | ASTM D2457 | |
| 45 °, 38.1 µm, blown film | 25 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 12.7 µm, blown film | 25 | % | ASTM D1003 |
| 38.1 µm, blown film | 30 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from blown film produced at a 2.5:1 BUR, 360°F melt temperature, using an 8 in die with 0.025 in die gap, at 150 lb/hr. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime 6600 NAT | Prime PVC® | PVC, Rigid | Prime |
| APEX® 86-K853-A | Teknor Apex Company | PVC, Flexible | APEX® |
| FM® 410-1 | Cytec Industries Inc. | Epoxy | FM® |
| Hytrel® PC988 NC010 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Karina CLEAR PVC COMPOUND -E 75/218-D-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |