LubriOne™ NL-30CF/15T Black
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gIW2GW_LubriOne-NL-30CF-15T-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 1.0 | % | |
| Across Flow | 1.0 to 2.0 | % | |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 19300 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 169 | MPa | |
| Break 2 | 169 | MPa | |
| Tensile Elongation 3(Break) | 2.9 | % | ASTM D638 |
| Flexural Modulus | 14500 | MPa | ASTM D790 |
| Flexural Strength | 269 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.14 | ||
| vs. Steel - Static | 0.26 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm, Injection Molded) | 100 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 212 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 198 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+3 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 243 to 271 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 4017 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Sylvin 5162-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nypol® PA A3 G30 PRTA011 NR398 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| ACCUTECH™ SAN930G40L | ACLO Compounders Inc. | SAN | ACCUTECH™ |
| Epic Urethane S7475 | Epic Resins | PUR, Unspecified | Epic Urethane |