Novalloy-S S5220
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Novalloy-S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gIPNrB_Novalloy-S-S5220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Novalloy-S S5220 is a Polycarbonate + ABS (PC+ABS) product filled with 20% glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 97.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 5980 | MPa | ASTM D790 |
| Flexural Strength | 134 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 133 | °C | ASTM D648 |
| CLTE - Flow | 4.1E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.65 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LAP274 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Dugdale PVC Rigid Extrusion Black Compound | Dugdale Plc | PVC, Rigid | Dugdale PVC |
| Hifax TYC 007P E C13097 | LyondellBasell Industries | PP Copolymer | Hifax |
| Plenco 03356 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |
| KetaSpire® KT-880 FW30 | Solvay Specialty Polymers | PEEK | KetaSpire® |