Order Products : sales@su-jiao.com
Sindustris PBT TE5001HZ
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gI0at2_Sindustris-PBT-TE5001HZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PBT TE5001HZ is a Polycarbonate + PBT (PC+PBT) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PBT TE5001HZ are:
Typical application of Sindustris PBT TE5001HZ: Automotive |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 59.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 100 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2160 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 83.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 95.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 110 | °C | |
| Peak Melting Temperature | 225 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 250 to 260 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 255 to 260 | °C | |
| Nozzle Temperature | 260 to 270 | °C | |
| Processing (Melt) Temp | 260 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Prime Series NG15-01NC | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Formolene FORMAX® L71709A | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene FORMAX® |
| Elastron® G P.G401.A30.N | Elastron USA, Inc. | SEBS | Elastron® G |
| LEXAN™ EX9332T resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| PELPRENE™ P30B | TOYOBO America, Inc. | TPEE | PELPRENE™ |