KetaSpire® KT-820 SL10

Category:	PEEK , Polyetheretherketone
Manufacturer:	Solvay Specialty Polymers
Trademark:	KetaSpire®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	gH8Yip_KetaSpire-KT-820-SL10.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
KetaSpire® KT-820 SL10 is a polyetheretherketone (PEEK) based compound designed to offer enhanced lubricity and reduced friction compared to standard PEEK. Unlike other grades formulated for wear resistance, this grade offers high lubricity while retaining outstanding ductility and toughness that surpasses that of unmodified high viscosity PEEK. Also, this product offers high melt flow, which allows injection molding of thin, intricate, or complex parts. In addition to these differentiating features, this resin also offers the outstanding combination of ultra-performance attributes commonly known for PEEK. These include: mechanical strength and stiffness even at elevated temperatures, long term thermal-oxidative stability, fatigue resistance, and excellent chemical resistance to a broad range of harsh chemical environments including acids, bases, and organics. The attractive combination of properties make KetaSpire® KT-820 SL10 suitable for applications in transportation, electronics, chemical processing, and industrial uses including oil and gas exploration and production.

Message

KetaSpire® KT-820 SL10 is a polyetheretherketone (PEEK) based compound designed to offer enhanced lubricity and reduced friction compared to standard PEEK. Unlike other grades formulated for wear resistance, this grade offers high lubricity while retaining outstanding ductility and toughness that surpasses that of unmodified high viscosity PEEK. Also, this product offers high melt flow, which allows injection molding of thin, intricate, or complex parts.

In addition to these differentiating features, this resin also offers the outstanding combination of ultra-performance attributes commonly known for PEEK. These include: mechanical strength and stiffness even at elevated temperatures, long term thermal-oxidative stability, fatigue resistance, and excellent chemical resistance to a broad range of harsh chemical environments including acids, bases, and organics.

The attractive combination of properties make KetaSpire® KT-820 SL10 suitable for applications in transportation, electronics, chemical processing, and industrial uses including oil and gas exploration and production.

General Information
Features	Fatigue Resistant Flame Retardant Good Chemical Resistance Good Dimensional Stability Good Wear Resistance High Heat Resistance
Uses	Film Industrial Applications Oil/Gas Applications Profiles Rods Sheet Tubing
RoHS Compliance	RoHS Compliant
Appearance	Black
Forms	Pellets
Processing Method	Injection Molding Machining Profile Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.35	g/cm³	ASTM D792
Molding Shrinkage			ASTM D955
Flow : 3.20 mm ¹	1.2 to 1.4	%
Across Flow : 3.20 mm ²	1.6 to 1.8	%
Water Absorption (24 hr)	0.10	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 1 sec)	83		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ³	3600	MPa	ASTM D638
Tensile Strength ⁴	88.0	MPa	ASTM D638
Tensile Elongation
Yield ⁵	5.2	%	ASTM D638
Break ⁶	60	%	ASTM D638
Break	60	%	ISO 527-2/1A/50
Flexural Modulus	3500	MPa	ASTM D790
Flexural Strength			ASTM D790
--	134	MPa
Yield	134	MPa

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	170	J/m	ASTM D256
Unnotched Izod Impact	No Break		ASTM D4812

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed)	155	°C	ASTM D648

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C, 1000 sec^-1)	170	Pa·s	ASTM D3835

Injection	Nominal Value	Unit
Drying Temperature	150	°C
Drying Time	4.0	hr
Rear Temperature	365	°C
Middle Temperature	370	°C
Front Temperature	375	°C
Nozzle Temperature	380	°C
Mold Temperature	175 to 205	°C
Injection Rate	Fast
Screw Compression Ratio	2.5:1.0 to 3.5:1.0

Note Message
1 .	5" x 0.5" x 0.125" bars
2 .	5" x 0.5" x 0.125" bar
3 .	50 mm/min
4 .	50 mm/min
5 .	50 mm/min
6 .	50 mm/min

Resin Grade	Manufacturer	Category	Trademark
Rotec® ABS 3001	ROMIRA GmbH	ABS	Rotec® ABS
TRIEL® 5500	Samyang Corporation	TPEE	TRIEL®
NuSil R-2188	NuSil Technology	Silicone	NuSil
KUBE PIR 22414	KUBE Electronics AG	HDPE	KUBE PIR
Sylvin 9604-90 Grey 9538	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin

Resin Grade

Manufacturer