Bayfit® 49BM02(90 Index, 86 kg/m³)
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayfit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGwsbm_Bayfit-49BM02-90-Index-86-kg-m-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyol formulation intended for processing with isocyanates to produce visco-elastic moulded polyurethane foam with slow recovery after compression. Potential fields of application are mattresses and cushioning for the furniture industry. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Core Density | 86.0 | kg/m³ |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Hardness - cv40 | 5.60 | ||
| Hysteresis - h70 | 61 | % |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | 0.196 | MPa | |
| Tensile Elongation (Break) | 160 | % | |
| Tear Strength | 0.379 | kN/m | |
| Compression Set 1 | 2.0 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Hydroxyl Number, PET-11-01: 137 to 151 mg KOH/gWater Content, PET-19-01: 1.70 to 2.00%Density, PET-07-01: approx. 1.05 g/cm³Color: colorless, slightly yellowish, clearOdor: slightly like amineProcessing data (lab foaming): Temperature of raw materials: 25°C Cream Time: 11 sec Gel Time: 85 sec Rise Time: approx. 150 sec Mould Temperature: approx. 55°C Processing conditions for high pressure equipment: Mold Temperature: 50 to 60°C Molded Density: 70 to 95 kg/m³ Mixing Ratios: 100:52 to 100:59 Demold Time: 6 to 7 min Temperature of raw materials: 20 to 30°C |
| Note Message | |
|---|---|
| 1 . | at 75% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® MJ5302C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| TIPPLEN® H 781 F | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| Vandar® 6000 | Celanese Corporation | PBT | Vandar® |
| Dryflex® A2 602709 | ELASTO | SEBS | Dryflex® |
| LNP™ THERMOCOMP™ DX06313I compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |