Complet® LCF30-PA6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PlastiComp, Inc. |
| Trademark: | Complet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGw2ZX_Complet-LCF30-PA6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Complet®LCF30-PA6 is a polyamide 6 (nylon 6) product, which contains a 30% long carbon fiber as a filler. It is available in North America, Europe or Asia Pacific. The main features are: Rohs certification. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 22100 | MPa | ASTM D638 |
| Tensile Strength | 269 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus | 16200 | MPa | ASTM D790 |
| Flexural Strength | 379 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 210 | J/m | ASTM D256 |
| Unnotched Izod Impact | 910 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.18 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 260 - 277 | °C | |
| Middle Temperature | 266 - 282 | °C | |
| Front Temperature | 271 - 288 | °C | |
| Nozzle Temperature | 271 - 288 | °C | |
| Processing (Melt) Temp | 271 - 288 | °C | |
| Mold Temperature | 93.3 | °C | |
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 30 - 50 | rpm | |
| Cushion | 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 to 20.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| Injection speed: 2 to 3 in/secInjection pressure: medium to maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP611M | Southern Polymer, Inc. | mLLDPE | PRIMALENE |
| Resinoid 2215 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| KYOCERA CT4112 | KYOCERA Chemical Corporation | PI, TS | KYOCERA |
| LNP™ THERMOCOMP™ WF004 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| Hostacom CR 250 F C11432 | LyondellBasell Industries | PP, Unspecified | Hostacom |