AMPLIFY™ TY 1052H

Category:	MAH-g , Functional Polymer
Manufacturer:	The Dow Chemical Company
Trademark:	AMPLIFY™ TY
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	gGX9kG_AMPLIFY-TY-1052H.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
AMPLIFY™ TY 1052H Functional Polymer is a maleic anhydride grafted (MAH) polymer concentrate designed as a blend component for unmodified polyethylene and polypropylene. In tie layers for flexible packaging, AMPLIFY TY 1052H Functional Polymer promotes adhesion of polyethylene and polypropylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH). The functionality of this polymer also promotes adhesion between metal, polyolefins, cellulose, polyester, polycarbonate, glass, and foil. Typical blending levels in polyethylene let-down resin are 20-25% for EVOH and 10-15% for nylon. Main Characteristics: Adhesive concentrate for use in blown, cast, and coating applications Tie layer for food packaging and pipe coating Adhesive layer in multi-layer flexible film applications Polymer compatibilizer Complies with: U.S. FDA 21 CFR 175.105 EU, No 10/2011 Consult the regulations for complete details.

Message

AMPLIFY™ TY 1052H Functional Polymer is a maleic anhydride grafted (MAH) polymer concentrate designed as a blend component for unmodified polyethylene and polypropylene. In tie layers for flexible packaging, AMPLIFY TY 1052H Functional Polymer promotes adhesion of polyethylene and polypropylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH). The functionality of this polymer also promotes adhesion between metal, polyolefins, cellulose, polyester, polycarbonate, glass, and foil.

Typical blending levels in polyethylene let-down resin are 20-25% for EVOH and 10-15% for nylon.

Main Characteristics:

Adhesive concentrate for use in blown, cast, and coating applications

Tie layer for food packaging and pipe coating

Adhesive layer in multi-layer flexible film applications

Polymer compatibilizer

Complies with:

U.S. FDA 21 CFR 175.105

EU, No 10/2011

Consult the regulations for complete details.

General Information
Agency Ratings	FDA 21 CFR 175.105 Europe No 10/2011
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	0.875	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.3	g/10 min	ASTM D1238, ISO 1133
MAH Graft Level ¹	High		Internal method

Hardness	Nominal Value	Test Method
Durometer Hardness		ASTM D2240, ISO 868
Shaw A	77	ASTM D2240, ISO 868
Shaw D	21	ASTM D2240, ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	8.96	MPa	ASTM D638, ISO 527-2/51
Tensile Elongation (Break)	1000	%	ASTM D638, ISO 527-2/51
Flexural Modulus - 2% Secant	13.8	MPa	ASTM D790A, ISO 178

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	40.0	°C	ASTM D1525, ISO 306
Melting Temperature (DSC)	62.8	°C	Internal method

Additional Information
Molded in accordance with ASTM D4976.

Note Message
1 .	Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt%, Very High >1.0 wt%.

Resin Grade	Manufacturer	Category	Trademark
Radilon® AGV 25 Natural	Radici Plastics	Nylon 66	Radilon®
DeWAL DW 202	DeWAL Industries	PTFE	DeWAL
LNP™ STAT-KON™ MFD02 compound	SABIC Innovative Plastics	PP, Unspecified	LNP™ STAT-KON™
Lupol® HI5302RB	LG Chem Ltd.	TPO	Lupol®
Akulon® S223-HG0	DSM Engineering Plastics	Nylon 66	Akulon®