Eraclene® MM 80 U
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Eraclene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGVOnq_Eraclene-MM-80-U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eraclene MM 8O U is a high density polyethylene resin (HDPE) with antioxidants, suitable for injection moulding application. Eraclene MM 80 U is characterized by high rigidity and good impact resistance. Main Application Eraclene MM 8O U is specifically designed for pails and light-weight containers. Moreover, the product is suitable to manufacture dustbins and small industrial containers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 5.5 | g/10 min | |
| 190°C/5.0 kg | 14 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 28.0 | MPa | |
| Break, Compression Molded | 20.0 | MPa | |
| Tensile Strain (Break, Compression Molded) | 550 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 1350 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(Compression Molded) | 110 | J/m | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ISO 306/A |
| Melting Temperature | 135 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 220 to 275 | °C | |
| Middle Temperature | 220 to 275 | °C | |
| Front Temperature | 220 to 275 | °C | |
| Mold Temperature | 10.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIREX® Compound 3025GRU10 | Samyang Corporation | PC | TRIREX® Compound |
| NOVAPOL® TF-0119 Series | NOVA Chemicals | LLDPE | NOVAPOL® |
| Karina WHITE PVC COMPOUND BR-11 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LG PVC PB1752 | LG Chem Ltd. | PVC Homopolymer | LG PVC |
| Monprene® RG-17250 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |