Elvaloy® AC 1126
| Category: | EMA , Ethylene Methyl Acrylate Copolymer |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Elvaloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGOftc_Elvaloy-AC-1126.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% Methyl Acrylate |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.944 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A | 78 | ||
| Shore D | 19 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 19.0 | MPa | ASTM D638 |
| -- | 19.0 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 14.0 | MPa | ISO 527-2/500 |
| -- 2 | 14.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break 3 | 860 | % | ASTM D638 |
| Break | 860 | % | ISO 527-2/500 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 45.0 | °C | ISO 306/A50, ASTM D1525 4 |
| Melting Temperature | 90.0 | °C | DSC, ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 220 | °C | |
| Cylinder Zone 5 Temp. | 290 | °C | |
| Adapter Temperature | 290 | °C | |
| Die Temperature | 290 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOND 5017 | SILON s.ro | LLDPE | TABOND |
| HAIPLEN H90 X2 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Kpren 135C | Shandong Xuye New Materials Co., Ltd. | CPE | Kpren |
| Latistat 67-08 | LATI S.p.A. | Nylon 66 | Latistat |
| POLYfill PP CCP20020 UV | Polykemi AB | PP, Unspecified | POLYfill |