INEOS Wire & Cable BPD3669

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	INEOS Wire & Cable
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	gGAEKK_INEOS-Wire-Cable-BPD3669.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

LLDPE with enhanced properties for crosslinked low voltage cable insulation

Applications

BPD3669 is a LLDPE copolymer containing hexene-1 as comonomer which, when compounded with suitable additives, is designed for silane crosslinked LV insulation. BPD3669 can be used in a silane one step cross-linking process (Monosil® for example) and in a silane two step crosslinking process (Sioplas® process).

BPD3669 has been developed specifically to provide enhanced crosslinking and extrusion performances, thanks to proprietary process and catalyst and fit for purpose product design.

LLDPE with enhanced properties for high performance cable jacketing

Applications

BPD3669 is a LLDPE which, when compounded with suitable additives, is designed for jacketing of cables, especially power cables.

BPD3669 combines an enhanced environmental stress cracking resistance to excellent mechanical properties.

General Information
Features	Copolymer Crosslinkable Hexene Comonomer High ESCR (Stress Crack Resist.) Low Density
Uses	Cable Jacketing Low Voltage Insulation Wire & Cable Applications
Agency Ratings	ASTM D 1248, I, Class A, Cat. 3 ISO 1872 PE KGN 18D045
Forms	Pellets
Processing Method	Wire & Cable Extrusion

Physical	Nominal Value	Unit	Test Method
Density (23°C)	0.926	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	3.3	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance (10% Igepal, F0)	> 1000	hr	IEC 60811-406

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D, 1 sec)	56		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress
Break	30.0	MPa	ISO 527-2
Break, 23°C ¹	28.0	MPa	ISO 527-2/50
Tensile Strain
Break	800	%	ISO 527-2
Break, 23°C ²	500	%	ISO 527-2/50

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	-76.0	°C	ISO 974
Hot Set - 15 min, 0.2 MPa ³(200°C)	60	%	IEC 60811-507

Electrical	Nominal Value		Test Method
Dielectric Constant (1 MHz)	2.30		ASTM D1531
Dissipation Factor (1 MHz)	7.0E-5		ASTM D1531

Note Message
1 .	Crosslinked
2 .	Crosslinked
3 .	Crosslinked

Resin Grade	Manufacturer	Category	Trademark
Zhongfa PP pp6	Yuyao Zhongfa Engineering Plastics Co. Ltd.	PP, Unspecified	Zhongfa
Dynaflex™ D3202-1000-03	PolyOne Corporation	TPE	Dynaflex™
LEXAN™ HPF1 resin	SABIC Innovative Plastics	PC	LEXAN™
LUVOCOM® 1105-7794/BL VP	Lehmann & Voss & Co.	PEEK	LUVOCOM®
LUVOCOM® 80-7580/BK VP	Lehmann & Voss & Co.	Acetal (POM) Copolymer	LUVOCOM®