LEXAN™ 263F resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gFp16r_LEXAN263Fresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LEXAN 263F is a medium viscosity multi purpose UV stabilized grade with improved release performance. This grade is UL94-V2 at 0.8 mm approved. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Fracture | 70.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture | 120 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2300 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 3 | 14 | kJ/m² | ISO 179/1eA |
| 23°C 4 | 73 | kJ/m² | ISO 179/1eA |
| 23°C | 35 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact 6 | ISO 180/1A | ||
| -30°C | 12 | kJ/m² | ISO 180/1A |
| 23°C | 70 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, unannealed, 100 mm span | 138 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 127 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ISO 306/B50 |
| -- | 145 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (23 to 80°C) | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.70 | IEC 60250 | |
| 60 Hz | 2.70 | IEC 60250 | |
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm | V-2 | UL 94 | |
| 6.0 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.0 mm) | 850 | °C | IEC 60695-2-12 |
| Oxygen Index | 25 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ISO 489 | |
| Transmittance (2540 µm) | 88.0 - 90.0 | % | ASTM D1003 |
| Haze (2540 µm) | < 0.80 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60 - 80 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 280 - 310 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80 - 110 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*3 sp=62mm |
| 4 . | 80*10*3 sp=62mm |
| 5 . | 80*10*3 sp=62mm |
| 6 . | 80*10*3 |
| 7 . | 80*10*3 |
| 8 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 208A | RTP Company | Nylon 6 | RTP |
| Sarlink® TPE EE-2260N NAT | Teknor Apex Company | TPE | Sarlink® TPE |
| Ultramid® 8233G HS BK-106 | BASF Corporation | Nylon 6 | Ultramid® |
| HANWHA EVA 1826 | Hanwha Chemical | EVA | HANWHA EVA |
| Dutral® TX 1301 | Versalis S.p.A. | EPDM | Dutral® |