Durethan® BM 40 X H2.0 EF 900116
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gFW0FS_DurethanBM40XH20EF900116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 40 % glass fibers/mineral, injection molding, improved flowability, heat-aging stabilized, low tendency to warp, improved surface finish |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.45 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 290°C, 2.00mm 1 | 0.72 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.11 | -- | % | ISO 2577 |
| Flow direction : 290°C, 2.00mm 3 | 0.31 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.050 | -- | % | ISO 2577 |
| Vertical flow direction : 290°C, 3.00mm 5 | 0.87 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 3.00mm 6 | 0.15 | -- | % | ISO 2577 |
| Flow direction : 290°C, 3.00mm 7 | 0.25 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 3.00mm 8 | 0.050 | -- | % | ISO 2577 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 210 | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9000 | 4500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 125 | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | 8.7 | % | ISO 527-2/5 |
| Flexural Modulus 9(23°C) | 8800 | 4250 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | 200 | 110 | MPa | ISO 178/A |
| 23°C 10 | 206 | 125 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 11(23°C) | 2.9 | 6.2 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 10-080, (GF+MD) 40 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | -- | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 37 | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 40 | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | -- | kJ/m² | ISO 180/1A |
| 23°C | < 10 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 33 | 30 | kJ/m² | ISO 180/1U |
| 23°C | 35 | 60 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 195 | -- | °C | ISO 75-2/A |
| Melting Temperature 12 | 220 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.8E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 8.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 150x105x3mm, 80°C MT, 500 bar |
| 6 . | 150x105x3mm |
| 7 . | 150x105x3mm, 80°C MT, 500 bar |
| 8 . | 150x105x3mm |
| 9 . | 2.0 mm/min |
| 10 . | 2.0 mm/min |
| 11 . | 2 mm/min |
| 12 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA612 A5G6301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 612 | Shandong PA612 |
| Sinvicomp SRF3834 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| AMTOPP KM35 | Inteplast Group | PP, Unspecified | AMTOPP |
| FORMEX® GK-62 | ITW FORMEX | PP, Unspecified | FORMEX® |
| Sylvin 8773-60D Red 6235 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |