| Low emission polypropylene homopolymer reinforced with 30% chemically coupled glass fiber, high thermal resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.20 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 6200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 146 | °C | ASTM D648 |
| Vicat Softening Temperature | 134 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide AG5 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Addisil™ 2070 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Extir® LN 2000 | Versalis S.p.A. | PS (EPS) | Extir® |
| EL-Lene™ H5211PYL | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| Maxxam™ PP5940 B131 C 600R | PolyOne Corporation | PP, Unspecified | Maxxam™ |