NORYL™ 731 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gEyk3K_NORYL731resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL 731 is an unfilled material, with a Vicat B/120 of 140C according ISO 306. NORYL 731 is a general purpose material with good balance of Strength, Impact and Flow. NORYL 731 is available in all colours. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.23 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 100 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | ISO 527-2/50 |
| Fracture | 30 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2200 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 65.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 15 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 4 | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 15 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 100 mm span | 130 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 115 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 145 | °C | ISO 306/A50 |
| -- | 135 | °C | ISO 306/B50 |
| -- | 140 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | IEC 60695-10-2 | |
| 133°C 6 | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.22 | W/m/K | ISO 8302 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 19 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.70 | IEC 60250 | |
| 60 Hz | 2.70 | IEC 60250 | |
| 1 MHz | 2.60 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 2.0E-3 | IEC 60250 | |
| 60 Hz | 2.0E-3 | IEC 60250 | |
| 1 MHz | 1.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 22 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 260 - 280 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Hopper Temperature | 40.0 - 60.0 | °C | |
| Cylinder Zone 1 Temp. | 220 - 240 | °C | |
| Cylinder Zone 2 Temp. | 230 - 250 | °C | |
| Cylinder Zone 3 Temp. | 250 - 270 | °C | |
| Cylinder Zone 4 Temp. | 250 - 270 | °C | |
| Adapter Temperature | 250 - 270 | °C | |
| Melt Temperature | 250 - 270 | °C | |
| Die Temperature | 250 - 270 | °C | |
| Calibration Temp, First | 60.0 - 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| 6 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EXTEM™ UH1006M resin | SABIC Innovative Plastics Europe | PI, TP | EXTEM™ |
| KRATON® D2122 DO | Kraton Polymers LLC | SBS | KRATON® |
| Sylvin 8200-70 White 1452 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| OTECH PVC OM5017-Molding | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| Zytel® BM7300THS BK317 | DuPont Performance Polymers | Nylon 6 | Zytel® |