| CAPRAN® 1500 is a 0.59 mil (15 micron) biaxially oriented nylon 6 film with excellent flex crack resistance and superior clarity properties well suited for packaging applications requiring excellent mechanical strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.22 | ASTM D1894 | |
| With self-dynamics | 0.70 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| secant modulus | ASTM D882 | ||
| MD : 15 µm | 2760 | MPa | ASTM D882 |
| TD : 15 µm | 2760 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 15 µm | 262 | MPa | ASTM D882 |
| TD : Break, 15 µm | 262 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 15 µm | 80 | % | ASTM D882 |
| TD : Break, 15 µm | 80 | % | ASTM D882 |
| Oxygen Permeability (23°C, 15 µm) | 1.4 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (15 µm, 38°C, 100% RH) | 330 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 15.0 µm) | 160 - 175 | ASTM D2457 | |
| Haze (15.0 µm) | 2.2 - 3.3 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield: 40800 in²/lbTensile Strength @ Break, ASTM D 882, MD: 34000 to 42000 psiTensile Strength @ Break, ASTM D 882, TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD: 70 to 90%Elongation @ Break, ASTM 882, TD: 70 to 90%Secant Modulus, ASTM D 882, MD: 350000 to 450000 psiSecant Modulus, ASTM D 882, TD: 350000 to 450000 psiGraves Tear (initial), ASTM D 1004, MD: 1100 to1500 g/milGraves Tear (initial), ASTM D 1004, TD: 1000 to1500 g/milCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicSurface Tension, ASTM D5946, treated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, untreated side: >50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: 0.2 to 0.7% shrinkageWater Vapor Transmission ASTM F1249, 100°F, 100%RH: 20 to 23 g/100 in²/day |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene MDPE 3802 (Blow Molding) | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| Mytex® AS33L(W)-06 | Mytex Polymers | PP, Unspecified | Mytex® |
| NEOFLON™ EP-506 | Daikin Fluorochemicals (China) Co., Ltd. | ETFE | NEOFLON™ |
| COPYLENE® CR750CL-02 | Phillips 66 | PP Random Copolymer | COPYLENE® |
| ExxonMobil™ NTX 101 | ExxonMobil Chemical | LLDPE | ExxonMobil™ |