MFE® -7
| Category: | Vinyl Ester , Vinyl Ester |
| Manufacturer: | Huachang Polymer Co., Ltd. |
| Trademark: | MFE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gDVQla_MFE--7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MFE-7 is a bromated bisphenol-A epoxy vinyl ester with excellent fire retardancy. Both filled and non-filled fire-retardant epoxy vinyl ester resins are available based on MFE-7 resin. PROPERTY
APPLICATION
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Acid Value | 8.00 to 16.00 | mg KOH/g | |
| Solids Content | 58 to 64 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability (80°C) | > 1 | day |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Gel Time (25°C) | 15.0 to 25.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Gel to Peak | 8.0 to 12.0 | min | |
| Peak Exotherm | 150 to 180 | °C | |
| Sb2O3 | 3.0 to 5.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ASTM D638 |
| Tensile Strength | 75.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus | 3500 | MPa | ASTM D790 |
| Flexural Strength | 130 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity (25°C) | 300 to 500 | cP |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AT 280 | Celanese EVA Performance Polymers | LDPE | AT |
| Generic LCP - Glass Fiber | Generic | LCP | Generic |
| LNP™ LUBRICOMP™ QAP22S compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |
| TORZEN® HV125A NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Romiloy® 1035/07 GF10 | ROMIRA GmbH | PC+ABS | Romiloy® |