Fibremod™ GB306SAF
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gD0ON9_Fibremod-GB306SAF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibremod GB306SAF is a 35 % chemically coupled high performance glass fibre reinforced polypropylene compound intended for injection moulding. The product is available in standard black 9502. This material shows excellent mechanical properties also at elevated temperatures. Applications: Fibremod GB306SAF has been developed especially for demanding applications in under the bonnet applications.
Features: Long term high heat stabilized Copper (CU) stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Vertical flow direction : 2.00mm | 0.80 - 1.2 | % | Internal method |
| Flow direction : 2.00mm | 0.10 - 0.20 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 9000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 118 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, Injection Molded) | 2.8 | % | ISO 527-2/50 |
| Flexural Modulus 2(Injection Molded) | 8000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C, injection molding | 10 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C, injection molding | 54 | kJ/m² | ISO 179/1eU |
| 23°C, injection molding | 58 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C, injection molding | 10 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 154 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 142 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 280 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 to 80°CBack pressure: As low as possibleScrew speed: Low to mediumFlow front speed: 100 to 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 150x80x2 mm |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVASTER® C FRU 2 | Plastcom | PC | SLOVASTER® |
| Viprene™ P60A-22U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| Zytel® 73G15HSL BK363 | DuPont Performance Polymers | Nylon 6 | Zytel® |
| Evoprene™ LF 6154 | AlphaGary | SBC | Evoprene™ LF |
| Karina YELLOW PVC COMPOUND 752D02/101-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |