Exelene® PP C2004
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Montachem International, Inc. |
| Trademark: | Exelene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gCqoSq_Exelene-PP-C2004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications:
Characteristics:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 21.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 7.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(3.20 mm) | 896 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 4(0.45 MPa, Unannealed) | 86.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 143 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Method I (3 point load), 13 mm/min |
| 4 . | 2°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hapflex™ 871 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| KPOL-PP K-PPH 1.80 | KPOL Chem Co. | PP Homopolymer | KPOL-PP |
| Kumsollan® KSE5090 | Shanghai KumhoSunny Plastics Co., Ltd. | SEBS | Kumsollan® |
| Lucky Enpla LAY1004H | Lucky Enpla Co LTD | PC+ABS | Lucky Enpla |
| Plasmer 1045NM/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |